Cronatron® 41 Silver Flux Coated Brazing Rod 3/32"
Cronatron® - 41 Silver Flux Coated Brazing Rod, Red, 18" Length, 3/32" (6 Feet)
Welcome. Register now to see your pricing.
Close
Cronatron® - 41 Silver Flux Coated Brazing Rod, Red, 18" Length, 3/32" (6 Feet)
With lower melting temperatures and better capillary action than low silver products, medium silver brazing alloys are excellent for joining copper, stainless steel, bronze alloys and nickel alloys.
Superior Advantages
Thin-flowing for tight joints, yet fills and bridges gaps
Strong and ductile
Very good electrical conductivity
Low-temperature application
Flux Coating Color: RedTensile Strength: 80,000 PSIBrazing Range: 1,120°F to 1,150°F (604°C to 621°C)Recommended Flux: F40 (if needed)
Typical Applications
Electrical rotors, contacts and lugs
Instrumentation and controls
Plumbing
Arts and crafts
Stainless steel
Usage ProcedureMaterials should be smooth and free of burrs or uneven edges. A carburizing oxyacetylene flame should be used, heating a broad surface along the joint line. Keep the flame cone one inch ahead of the alloy rod and a continuous fillet will form. Clean flux residue off with water.
With lower melting temperatures and better capillary action than low silver products, medium silver brazing alloys are excellent for joining copper, stainless steel, bronze alloys and nickel alloys.
Superior Advantages
Thin-flowing for tight joints, yet fills and bridges gaps
Strong and ductile
Very good electrical conductivity
Low-temperature application
Flux Coating Color: RedTensile Strength: 80,000 PSIBrazing Range: 1,120°F to 1,150°F (604°C to 621°C)Recommended Flux: F40 (if needed)
Typical Applications
Electrical rotors, contacts and lugs
Instrumentation and controls
Plumbing
Arts and crafts
Stainless steel
Usage ProcedureMaterials should be smooth and free of burrs or uneven edges. A carburizing oxyacetylene flame should be used, heating a broad surface along the joint line. Keep the flame cone one inch ahead of the alloy rod and a continuous fillet will form. Clean flux residue off with water.