Xl Gold All Steel Electrode Joins Disimialar Metals Tensile Up To 186000 Elongation 32% Polarity Dcep/Ac 97Rb To 35Rc Jobber Pack
(Pack of
1)
SKU:EG00194002 Item#: EG00194002
XL Gold is the standard in all-steel maintenance welding electrodes. XL Gold has higher strength, excellent elongation and superior weldability. It is easier to use, the slag is self-lifting, and the deposit has tougher crack resistance. XL Gold is the latest generation in all-steel welding electrodes
• Tougher welds - Duplex alloy with maximum crack resistance
• Higher tensile strength – 186,000 psi work hardened
• Improved welder appeal and slag removal with the exclusive Chem-A-Tized2 process
• Designed for welding difficult-to-weld steels like alloy steels and dissimilar types of steel
• All-position welding
• Tensile strength: Up to 186,000 psi work-hardened/1282 MPa, Up to 128,000 psi as deposited
• Yield strength: Up to 90,000 psi/620 MPa
• Elongation: 32%
• Reduction of area: 25%
• Machinability: Good with carbide tools
• Corrosion resistance: GoodHardness: As deposited 97Rb
• Work-hardened: 35 Rc
• Impact resistance: 100 ft-lbs. @ 75°F/25°C
• Heat resistance: Good up to 750°F/399°C
• Current: DCEP (DC+) or AC
Remove defective metal by grinding or gouging with Arc-Prep #161 electrode. Bevel heavy sections before welding. Use AC or DCEP current. Use a contact or a minimum arc length with a weave or stringer bead technique. Preheat should be used when the base metal requires it. For vertical-up welds reduce amperage slightly and use a modified weave technique. Chip the slag between multipass welds. Allow to cool slowly.
Frequently Bought Together
Product Description
XL Gold is the standard in all-steel maintenance welding electrodes. XL Gold has higher strength, excellent elongation and superior weldability. It is easier to use, the slag is self-lifting, and the deposit has tougher crack resistance. XL Gold is the latest generation in all-steel welding electrodes• Tougher welds - Duplex alloy with maximum crack resistance
• Higher tensile strength – 186,000 psi work hardened
• Improved welder appeal and slag removal with the exclusive Chem-A-Tized2 process
• Designed for welding difficult-to-weld steels like alloy steels and dissimilar types of steel
• All-position welding
• Tensile strength: Up to 186,000 psi work-hardened/1282 MPa, Up to 128,000 psi as deposited
• Yield strength: Up to 90,000 psi/620 MPa
• Elongation: 32%
• Reduction of area: 25%
• Machinability: Good with carbide tools
• Corrosion resistance: GoodHardness: As deposited 97Rb
• Work-hardened: 35 Rc
• Impact resistance: 100 ft-lbs. @ 75°F/25°C
• Heat resistance: Good up to 750°F/399°C
• Current: DCEP (DC+) or AC
Remove defective metal by grinding or gouging with Arc-Prep #161 electrode. Bevel heavy sections before welding. Use AC or DCEP current. Use a contact or a minimum arc length with a weave or stringer bead technique. Preheat should be used when the base metal requires it. For vertical-up welds reduce amperage slightly and use a modified weave technique. Chip the slag between multipass welds. Allow to cool slowly.
Technical Specifications
| Item#: | EG00194002 |
|---|---|
| Welding Process | Stick |
| Type | Stick |
| Diameter | 1/8 " |
| Tensile Strength | 186,000 PSI |
| Yield Strength | 90,000 PSI |
| Elongation | 32 % |
| Hardness | 35 HRC |
| Polarity | DCEP |
| Total | 2 lb |
| UNSPSC #: | 23271810 |
| TAA Compliant: | Yes |
| Weight: | 2.18 lb |