53 Pot Metal Bare Brazing Rod 1/16"
(Pack of
1.0)
Easily joins white and pot metals.
Superior Advantages
• Lead- and cadmium-free
• Extremely low melting point
• Two times stronger than ordinary solder
Low temperature, dissimilar pot metal
Tensile Strength: 17,500 PSIApplication Temperature: 360°F (182°C)Recommended Flux: F53
Typical Applications
• Air conditioning and refrigeration units
• Brazing/soldering of copper to aluminum, brass to steel, stainless to zinc, etc.
Usage ProcedureBase metal must supply heat, as a direct flame is unworkable. A carburizing flame should be used. A flux is required for all applications where good bonding is desired.
Technical TipDo not direct torch at flux, as it will char. Allow CRONABRAZE 53 to solidify before quenching and removing flux residue. CRONASOLV™ F53 flux is recommended for all applications.
Couldn't load pickup availability
California Proposition 65: Not Applicable
www.P65Warnings.ca.gov
Frequently Bought Together
241 Premium Aluminum Brazing Alloy 1/16x36
Couldn't load pickup availability
54 Aluminum Flux Cored Brazing Rod 1/8"
Couldn't load pickup availability
52 Aluminum/Zinc Bare Brazing Rod 1/8"
Couldn't load pickup availability
22 Cast Iron Bare Brazing Rod 3/16"
Couldn't load pickup availability
30 Copper and Steel Flux Coated Brazing Rod 3/32"
Couldn't load pickup availability
202Xl Red Flux Coated Brazing Alloy 3/16
Couldn't load pickup availability
Bumper Fascia General Purpose Split Rivet 3/16"
Couldn't load pickup availability
Front Fender Push-Type Retainer Nylon 20mm
Couldn't load pickup availability
Fender Bumper Shield Retainer 11/16"
Couldn't load pickup availability
Heat Stick 650F Degrees
Couldn't load pickup availability
Heat Stick 850F Degrees
Couldn't load pickup availability
Cap Whip-Lead Connector #4 to #1
Couldn't load pickup availability
Product Description
Easily joins white and pot metals.Superior Advantages
• Lead- and cadmium-free
• Extremely low melting point
• Two times stronger than ordinary solder
Low temperature, dissimilar pot metal
Tensile Strength: 17,500 PSIApplication Temperature: 360°F (182°C)Recommended Flux: F53
Typical Applications
• Air conditioning and refrigeration units
• Brazing/soldering of copper to aluminum, brass to steel, stainless to zinc, etc.
Usage ProcedureBase metal must supply heat, as a direct flame is unworkable. A carburizing flame should be used. A flux is required for all applications where good bonding is desired.
Technical TipDo not direct torch at flux, as it will char. Allow CRONABRAZE 53 to solidify before quenching and removing flux residue. CRONASOLV™ F53 flux is recommended for all applications.
Technical Specifications
| Item#: | CW1842 |
|---|---|
| Welding Process | Brazing |
| Type | Bare Brazing Rod |
| Diameter | 1/16 " |
| Tensile Strength | 17,500 PSI |
| Melting Temperature | 360 °F |
| Base Metal | Pot Metal |
| Recommended Flux | F53 |
| UNSPSC #: | 23271804 |
| TAA Compliant: | Yes |
| Weight: | 1.06 lb |
Product Restrictions
California Proposition 65: Not Applicable
www.P65Warnings.ca.gov