53 Bare Brazing Rod, Shiny Grey, 1/16" Diameter, Pot Metal
(Pack of
1)
SKU:CW1842 Item#: CW1842
Easily joins white and pot metals.
Superior Advantages
• Lead- and cadmium-free
• Extremely low melting point
• Two times stronger than ordinary solder
Low temperature, dissimilar pot metal
Tensile Strength: 17,500 PSI
Application Temperature: 360°F (182°C)
Recommended Flux: F53
Typical Applications
• Air conditioning and refrigeration units
• Brazing/soldering of copper to aluminum, brass to steel, stainless to zinc, etc.
Usage ProcedureBase metal must supply heat, as a direct flame is unworkable. A carburizing flame should be used. A flux is required for all applications where good bonding is desired.
Technical TipDo not direct torch at flux, as it will char. Allow CRONABRAZE 53 to solidify before quenching and removing flux residue. CRONASOLV™ F53 flux is recommended for all applications.
Frequently Bought Together
54 Aluminum Flux Cored Brazing Rod 1/8"
$0.00
Couldn't load pickup availability
52 Aluminum/Zinc Bare Brazing Rod 1/8"
$0.00
Couldn't load pickup availability
53 Pot Metal Bare Brazing Rod 1/8"
$0.00
Couldn't load pickup availability
23 Copper and Steel Flux Coated Brazing Rod 3/32"
$0.00
Couldn't load pickup availability
261 Blue Flux Coated General Purpose Silver Brazing Alloy 1/16X18
$0.00
Couldn't load pickup availability
265 Bare Silver Free Flowing Copper Alloy .050X20
$0.00
Couldn't load pickup availability
Rear Bumper Cover Retainer Plastic 18mm
$0.00
Couldn't load pickup availability
Bumper and Wheel Well Liner Push-Type Retainer
$0.00
Couldn't load pickup availability
Fender Apron Drive Rivet 8mm Hole
$0.00
Couldn't load pickup availability
Solid Solder 1/32"
$0.00
Couldn't load pickup availability
ER70S-6 Mild/Carbon Steel MIG Welding Wire 0.03"
$0.00
Couldn't load pickup availability
ER70S-6 Mild/Carbon Steel MIG Welding Wire 0.023"
$0.00
Couldn't load pickup availability
Product Description
Easily joins white and pot metals.Superior Advantages
• Lead- and cadmium-free
• Extremely low melting point
• Two times stronger than ordinary solder
Low temperature, dissimilar pot metal
Tensile Strength: 17,500 PSI
Application Temperature: 360°F (182°C)
Recommended Flux: F53
Typical Applications
• Air conditioning and refrigeration units
• Brazing/soldering of copper to aluminum, brass to steel, stainless to zinc, etc.
Usage ProcedureBase metal must supply heat, as a direct flame is unworkable. A carburizing flame should be used. A flux is required for all applications where good bonding is desired.
Technical TipDo not direct torch at flux, as it will char. Allow CRONABRAZE 53 to solidify before quenching and removing flux residue. CRONASOLV™ F53 flux is recommended for all applications.
Technical Specifications
| Item#: | CW1842 |
|---|---|
| Welding Process | Brazing |
| Type | Bare Brazing Rod |
| Diameter | 1/16 " |
| Tensile Strength | 17,500 PSI |
| Melting Temperature | 360 °F |
| Base Metal | Pot Metal |
| Recommended Flux | F53 |
| UNSPSC #: | 23271804 |
| TAA Compliant: | Yes |
| Weight: | 1.06 lb |